Temperature dependence of lasing properties of 8.3(3) at.% Yb:YSAG ceramics
Temperature dependence of the lasing properties of 8.3(3) at.% Yb:YSAG ceramics with various composition (Y2.35Yb0.25Sc1.00 Al4.4O12, Y1.95 Yb0.25 Sc1.00 Al4.8O12 and Y2.52Yb0.25Sc0.38Al4.5O12) have been studied. Study was carried out in a temperature range from 50°C to 125°C. The best lasing perfor...
保存先:
| 主要な著者: | , , , |
|---|---|
| フォーマット: | Статья |
| 言語: | English |
| 出版事項: |
Institute of Electrical and Electronics Engineers Inc.
2024
|
| 主題: | |
| オンライン･アクセス: | https://dspace.ncfu.ru/handle/123456789/29169 |
| タグ: |
タグ追加
タグなし, このレコードへの初めてのタグを付けませんか!
|
| 要約: | Temperature dependence of the lasing properties of 8.3(3) at.% Yb:YSAG ceramics with various composition (Y2.35Yb0.25Sc1.00 Al4.4O12, Y1.95 Yb0.25 Sc1.00 Al4.8O12 and Y2.52Yb0.25Sc0.38Al4.5O12) have been studied. Study was carried out in a temperature range from 50°C to 125°C. The best lasing performance has been achieved for the Y2.35 Yb0.25 Sc1.00 Al4.4 O12 ceramics, the maximum slope efficiency was 34 % and the optical efficiency was 25 %. |
|---|