Influence of MgO and CaO sintering additives on thermophysical, luminescent and optical properties of LuAG: Yb3+ laser ceramics

The precursor powder for laser ceramics Yb0.3Lu2.7Al5O12 were synthesized using the reverse chemical precipitation method. The influence of sintering additives CaO and MgO on the optical, thermophysical, and luminescent properties of the ceramics was investigated. The sintering process of ceramic po...

Popoln opis

Shranjeno v:

Bibliografske podrobnosti
Главные авторы:	Lapin, V. A., Лапин, В. А., Kravtsov, A. A., Кравцов, А. А., Suprunchuk, V. E., Супрунчук, В. Е., Tarala, L. V., Тарала, Л. В., Medyanik, E. V., Медяник, Е. В., Malyavin, F. F., Малявин, Ф. Ф.
Format:	Статья
Jezik:	English
Izdano:	Elsevier B.V. 2024
Teme:	Optical pumping Thermophysical Sintering Chemical precipitation method Laser ceramics Luminescent property MgO Optical - Precursor powder Property Sintering additives Synthesised Sintered alumina
Online dostop:	https://dspace.ncfu.ru/handle/123456789/29308
Oznake:	Označite Brez oznak, prvi označite!

Opis
Izvleček:	The precursor powder for laser ceramics Yb0.3Lu2.7Al5O12 were synthesized using the reverse chemical precipitation method. The influence of sintering additives CaO and MgO on the optical, thermophysical, and luminescent properties of the ceramics was investigated. The sintering process of ceramic powders with the Yb0.3Lu2.7Al5O12 composition was analyzed. When CaO was used as a sintering additive, aluminate phases with varying CaO–Al2O3 ratios formed on the surface of Yb0.3Lu2.7Al5O12 after high-temperature annealing in air. Laser radiation was generated in quasi-continuous pumping mode, achieving a power output of 2.9 W at an absorbed pumping power of 10.2 W using the Yb0.3Lu2.7Al5O12 ceramic active material.

Influence of MgO and CaO sintering additives on thermophysical, luminescent and optical properties of LuAG: Yb3+ laser ceramics

Podobne knjige/članki