Influence of MgO and CaO sintering additives on thermophysical, luminescent and optical properties of LuAG: Yb3+ laser ceramics

Influence of MgO and CaO sintering additives on thermophysical, luminescent and optical properties of LuAG: Yb3+ laser ceramics

The precursor powder for laser ceramics Yb0.3Lu2.7Al5O12 were synthesized using the reverse chemical precipitation method. The influence of sintering additives CaO and MgO on the optical, thermophysical, and luminescent properties of the ceramics was investigated. The sintering process of ceramic po...

وصف كامل

محفوظ في:
التفاصيل البيبلوغرافية
المؤلفون الرئيسيون: Lapin, V. A., Лапин, В. А., Kravtsov, A. A., Кравцов, А. А., Suprunchuk, V. E., Супрунчук, В. Е., Tarala, L. V., Тарала, Л. В., Medyanik, E. V., Медяник, Е. В., Malyavin, F. F., Малявин, Ф. Ф.
التنسيق: Статья
اللغة:English
منشور في: Elsevier B.V. 2024
الموضوعات:
Optical pumping
Thermophysical
Sintering
Chemical precipitation method
Laser ceramics
Luminescent property
MgO
Optical -
Precursor powder
Property
Sintering additives
Synthesised
Sintered alumina
الوصول للمادة أونلاين:https://dspace.ncfu.ru/handle/123456789/29308
الوسوم: إضافة وسم
لا توجد وسوم, كن أول من يضع وسما على هذه التسجيلة!

الانترنت

https://dspace.ncfu.ru/handle/123456789/29308

مواد مشابهة