Fabrication and characterization of LuAG: Er ceramics with high optical transmission

Fabrication and characterization of LuAG: Er ceramics with high optical transmission

Highly transparent ceramics based on LuAG with erbium content ranging from 1 to 50 at% were synthesized from powders prepared via chemical precipitation in an aqueous solution. The impact of hot isostatic pressing on the optical properties of these ceramics was investigated. It was demonstrated that...

Ausführliche Beschreibung

Gespeichert in:
Bibliographische Detailangaben
Hauptverfasser: Kravtsov, A. A., Кравцов, А. А., Chapura, O. M., Чапура, О. М., Tarala, V. A., Тарала, В. А., Medyanik, E. V., Медяник, Е. В., Tarala, L. V., Тарала, Л. В., Suprunchuk, V. E., Супрунчук, В. Е., Malyavin, F. F., Малявин, Ф. Ф., Kuznetsov, S. V., Кузнецов, С. В., Lapin, V. A., Лапин, В. А.
Format: Статья
Sprache:English
Veröffentlicht: Elsevier Ltd 2025
Schlagworte:
Ceramics
Thermal diffusivity
Hot isostatic pressing
LuAG
Luminescence
Optical properties
Online Zugang:https://dspace.ncfu.ru/handle/123456789/29617
Tags: Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
Beschreibung
Zusammenfassung:Highly transparent ceramics based on LuAG with erbium content ranging from 1 to 50 at% were synthesized from powders prepared via chemical precipitation in an aqueous solution. The impact of hot isostatic pressing on the optical properties of these ceramics was investigated. It was demonstrated that employing hot isostatic pressing enhances the optical transmittance of LuAG:Er ceramics. The influence of erbium concentration on the average grain size of the ceramics was also examined. Additionally, temperature-dependent thermal diffusivity profiles of LuAG:Er ceramics as a function of erbium content were analyzed. Erbium concentrations yielding the highest luminescence intensity in spectral ranges around ∼1.5–1.6 μm and ∼2.7 μm were determined.