Fabrication and characterization of LuAG: Er ceramics with high optical transmission

Highly transparent ceramics based on LuAG with erbium content ranging from 1 to 50 at% were synthesized from powders prepared via chemical precipitation in an aqueous solution. The impact of hot isostatic pressing on the optical properties of these ceramics was investigated. It was demonstrated that...

Volledige beschrijving

Bewaard in:

Bibliografische gegevens
Hoofdauteurs:	Kravtsov, A. A., Кравцов, А. А., Chapura, O. M., Чапура, О. М., Tarala, V. A., Тарала, В. А., Medyanik, E. V., Медяник, Е. В., Tarala, L. V., Тарала, Л. В., Suprunchuk, V. E., Супрунчук, В. Е., Malyavin, F. F., Малявин, Ф. Ф., Kuznetsov, S. V., Кузнецов, С. В., Lapin, V. A., Лапин, В. А.
Formaat:	Статья
Taal:	English
Gepubliceerd in:	Elsevier Ltd 2025
Onderwerpen:	Ceramics Thermal diffusivity Hot isostatic pressing LuAG Luminescence Optical properties
Online toegang:	https://dspace.ncfu.ru/handle/123456789/29617
Tags:	Voeg label toe Geen labels, Wees de eerste die dit record labelt!

Omschrijving
Samenvatting:	Highly transparent ceramics based on LuAG with erbium content ranging from 1 to 50 at% were synthesized from powders prepared via chemical precipitation in an aqueous solution. The impact of hot isostatic pressing on the optical properties of these ceramics was investigated. It was demonstrated that employing hot isostatic pressing enhances the optical transmittance of LuAG:Er ceramics. The influence of erbium concentration on the average grain size of the ceramics was also examined. Additionally, temperature-dependent thermal diffusivity profiles of LuAG:Er ceramics as a function of erbium content were analyzed. Erbium concentrations yielding the highest luminescence intensity in spectral ranges around ∼1.5–1.6 μm and ∼2.7 μm were determined.

Fabrication and characterization of LuAG: Er ceramics with high optical transmission

Gelijkaardige items