Fabrication and characterization of LuAG: Er ceramics with high optical transmission

Highly transparent ceramics based on LuAG with erbium content ranging from 1 to 50 at% were synthesized from powders prepared via chemical precipitation in an aqueous solution. The impact of hot isostatic pressing on the optical properties of these ceramics was investigated. It was demonstrated that...

Mô tả đầy đủ

Đã lưu trong:

Chi tiết về thư mục
Những tác giả chính:	Kravtsov, A. A., Кравцов, А. А., Chapura, O. M., Чапура, О. М., Tarala, V. A., Тарала, В. А., Medyanik, E. V., Медяник, Е. В., Tarala, L. V., Тарала, Л. В., Suprunchuk, V. E., Супрунчук, В. Е., Malyavin, F. F., Малявин, Ф. Ф., Kuznetsov, S. V., Кузнецов, С. В., Lapin, V. A., Лапин, В. А.
Định dạng:	Статья
Ngôn ngữ:	English
Được phát hành:	Elsevier Ltd 2025
Những chủ đề:	Ceramics Thermal diffusivity Hot isostatic pressing LuAG Luminescence Optical properties
Truy cập trực tuyến:	https://dspace.ncfu.ru/handle/123456789/29617
Các nhãn:	Thêm thẻ Không có thẻ, Là người đầu tiên thẻ bản ghi này!

Miêu tả
Tóm tắt:	Highly transparent ceramics based on LuAG with erbium content ranging from 1 to 50 at% were synthesized from powders prepared via chemical precipitation in an aqueous solution. The impact of hot isostatic pressing on the optical properties of these ceramics was investigated. It was demonstrated that employing hot isostatic pressing enhances the optical transmittance of LuAG:Er ceramics. The influence of erbium concentration on the average grain size of the ceramics was also examined. Additionally, temperature-dependent thermal diffusivity profiles of LuAG:Er ceramics as a function of erbium content were analyzed. Erbium concentrations yielding the highest luminescence intensity in spectral ranges around ∼1.5–1.6 μm and ∼2.7 μm were determined.

Fabrication and characterization of LuAG: Er ceramics with high optical transmission

Những quyển sách tương tự