Fabrication and characterization of LuAG: Er ceramics with high optical transmission

Fabrication and characterization of LuAG: Er ceramics with high optical transmission

Highly transparent ceramics based on LuAG with erbium content ranging from 1 to 50 at% were synthesized from powders prepared via chemical precipitation in an aqueous solution. The impact of hot isostatic pressing on the optical properties of these ceramics was investigated. It was demonstrated that...

全面介紹

Сохранить в:
書目詳細資料
Главные авторы: Kravtsov, A. A., Кравцов, А. А., Chapura, O. M., Чапура, О. М., Tarala, V. A., Тарала, В. А., Medyanik, E. V., Медяник, Е. В., Tarala, L. V., Тарала, Л. В., Suprunchuk, V. E., Супрунчук, В. Е., Malyavin, F. F., Малявин, Ф. Ф., Kuznetsov, S. V., Кузнецов, С. В., Lapin, V. A., Лапин, В. А.
格式: Статья
語言:English
出版: Elsevier Ltd 2025
主題:
Ceramics
Thermal diffusivity
Hot isostatic pressing
LuAG
Luminescence
Optical properties
在線閱讀:https://dspace.ncfu.ru/handle/123456789/29617
標簽: 添加標簽
沒有標簽, 成為第一個標記此記錄!
實物特徵
總結:Highly transparent ceramics based on LuAG with erbium content ranging from 1 to 50 at% were synthesized from powders prepared via chemical precipitation in an aqueous solution. The impact of hot isostatic pressing on the optical properties of these ceramics was investigated. It was demonstrated that employing hot isostatic pressing enhances the optical transmittance of LuAG:Er ceramics. The influence of erbium concentration on the average grain size of the ceramics was also examined. Additionally, temperature-dependent thermal diffusivity profiles of LuAG:Er ceramics as a function of erbium content were analyzed. Erbium concentrations yielding the highest luminescence intensity in spectral ranges around ∼1.5–1.6 μm and ∼2.7 μm were determined.

相似書籍