Highly transparent ceramics based on LuAG with erbium content ranging from 1 to 50 at% were synthesized from powders prepared via chemical precipitation in an aqueous solution. The impact of hot isostatic pressing on the optical properties of these ceramics was investigated. It was demonstrated that...

全面介绍

Сохранить в:
书目详细资料
Главные авторы: Kravtsov, A. A., Кравцов, А. А., Chapura, O. M., Чапура, О. М., Tarala, V. A., Тарала, В. А., Medyanik, E. V., Медяник, Е. В., Tarala, L. V., Тарала, Л. В., Suprunchuk, V. E., Супрунчук, В. Е., Malyavin, F. F., Малявин, Ф. Ф., Kuznetsov, S. V., Кузнецов, С. В., Lapin, V. A., Лапин, В. А.
格式: Статья
语言:English
出版: Elsevier Ltd 2025
主题:
Ceramics
Thermal diffusivity
Hot isostatic pressing
LuAG
Luminescence
Optical properties
在线阅读:https://dspace.ncfu.ru/handle/123456789/29617
标签: 添加标签
没有标签, 成为第一个标记此记录!
实物特征
总结:Highly transparent ceramics based on LuAG with erbium content ranging from 1 to 50 at% were synthesized from powders prepared via chemical precipitation in an aqueous solution. The impact of hot isostatic pressing on the optical properties of these ceramics was investigated. It was demonstrated that employing hot isostatic pressing enhances the optical transmittance of LuAG:Er ceramics. The influence of erbium concentration on the average grain size of the ceramics was also examined. Additionally, temperature-dependent thermal diffusivity profiles of LuAG:Er ceramics as a function of erbium content were analyzed. Erbium concentrations yielding the highest luminescence intensity in spectral ranges around ∼1.5–1.6 μm and ∼2.7 μm were determined.

相似书籍