Influence of the MgO/CaO Sintering Additive Ratio on the Optical Properties of YAG:Cr Ceramics
The influence of the content and ratio of MgO and CaO sintering additives on the optical properties of YAG:Cr3+ and YAG:Cr4+ ceramic materials was investigated. All samples showed high transparency at 1100 nm (more than 80%). However, in the approx. 340 nm region, the light transmittance values of t...
Сохранить в:
| Главные авторы: | , , , , , , , , , , , , , , , , , |
|---|---|
| Формат: | Статья |
| Язык: | English |
| Опубликовано: |
Springer
2025
|
| Темы: | |
| Online-ссылка: | https://dspace.ncfu.ru/handle/123456789/29835 |
| Метки: |
Добавить метку
Нет меток, Требуется 1-ая метка записи!
|
| Краткое описание: | The influence of the content and ratio of MgO and CaO sintering additives on the optical properties of YAG:Cr3+ and YAG:Cr4+ ceramic materials was investigated. All samples showed high transparency at 1100 nm (more than 80%). However, in the approx. 340 nm region, the light transmittance values of the samples decreased with increasing amounts of Ca2+ or Mg2+ ions. The most intense absorption in the range of 750 – 1100 nm after annealing in air was observed in the samples containing the highest value of sintering additives. The absorption of Cr4+ cations increased with the increase of Ca/Mg content. The optimum CaO content among the investigated samples was 0.12 wt.%. Above this value, additional absorption was observed due to the formation of microdefects. The data obtained by scanning electron microscopy showed that the ceramic samples had a granular structure with grain size ranging from 1 to 10 μm. There were no significant differences in the microstructure depending on the content and type of sintering additives. |
|---|