Yb:YSAG ceramics: An attractive thin-disk laser material alternative to a single crystal
The 8.3 at.% Yb-doped yttrium-scandium-aluminum garnet (YSAG) ceramics were fabricated by a modified reverse co-precipitation method followed by uniaxial and cold isostatic pressing, annealing in air and high-temperature sintering in vacuum. Spectroscopic and lasing properties were investigated in d...
Bewaard in:
| Hoofdauteurs: | , , , |
|---|---|
| Formaat: | Статья |
| Taal: | English |
| Gepubliceerd in: |
Elsevier Ltd
2024
|
| Onderwerpen: | |
| Online toegang: | https://dspace.ncfu.ru/handle/123456789/29243 |
| Tags: |
Voeg label toe
Geen labels, Wees de eerste die dit record labelt!
|
| Samenvatting: | The 8.3 at.% Yb-doped yttrium-scandium-aluminum garnet (YSAG) ceramics were fabricated by a modified reverse co-precipitation method followed by uniaxial and cold isostatic pressing, annealing in air and high-temperature sintering in vacuum. Spectroscopic and lasing properties were investigated in dependence on Y/Sc/Al ratio in ceramic composition. Optical transmission of Yb:YSAG ceramics in visible and near-infrared spectral range exceeds 80 % that indicates a high quality of the Yb:YSAG samples. Among all the ceramics, the Y2.35Yb0.25Sc1.00Al4.40O12 composition demonstrates the best lasing performance and the highest slope efficiency up to 75 %. |
|---|