Influence of MgO and CaO sintering additives on thermophysical, luminescent and optical properties of LuAG: Yb3+ laser ceramics

The precursor powder for laser ceramics Yb0.3Lu2.7Al5O12 were synthesized using the reverse chemical precipitation method. The influence of sintering additives CaO and MgO on the optical, thermophysical, and luminescent properties of the ceramics was investigated. The sintering process of ceramic po...

Ful tanımlama

Kaydedildi:

Detaylı Bibliyografya
Asıl Yazarlar:	Lapin, V. A., Лапин, В. А., Kravtsov, A. A., Кравцов, А. А., Suprunchuk, V. E., Супрунчук, В. Е., Tarala, L. V., Тарала, Л. В., Medyanik, E. V., Медяник, Е. В., Malyavin, F. F., Малявин, Ф. Ф.
Materyal Türü:	Статья
Dil:	English
Baskı/Yayın Bilgisi:	Elsevier B.V. 2024
Konular:	Optical pumping Thermophysical Sintering Chemical precipitation method Laser ceramics Luminescent property MgO Optical - Precursor powder Property Sintering additives Synthesised Sintered alumina
Online Erişim:	https://dspace.ncfu.ru/handle/123456789/29308
Etiketler:	Etiketle Etiket eklenmemiş, İlk siz ekleyin!

Diğer Bilgiler
Özet:	The precursor powder for laser ceramics Yb0.3Lu2.7Al5O12 were synthesized using the reverse chemical precipitation method. The influence of sintering additives CaO and MgO on the optical, thermophysical, and luminescent properties of the ceramics was investigated. The sintering process of ceramic powders with the Yb0.3Lu2.7Al5O12 composition was analyzed. When CaO was used as a sintering additive, aluminate phases with varying CaO–Al2O3 ratios formed on the surface of Yb0.3Lu2.7Al5O12 after high-temperature annealing in air. Laser radiation was generated in quasi-continuous pumping mode, achieving a power output of 2.9 W at an absorbed pumping power of 10.2 W using the Yb0.3Lu2.7Al5O12 ceramic active material.

Influence of MgO and CaO sintering additives on thermophysical, luminescent and optical properties of LuAG: Yb3+ laser ceramics

Benzer Materyaller