Fabrication and characterization of LuAG: Er ceramics with high optical transmission

Highly transparent ceramics based on LuAG with erbium content ranging from 1 to 50 at% were synthesized from powders prepared via chemical precipitation in an aqueous solution. The impact of hot isostatic pressing on the optical properties of these ceramics was investigated. It was demonstrated that...

Popoln opis

Shranjeno v:

Bibliografske podrobnosti
Главные авторы:	Kravtsov, A. A., Кравцов, А. А., Chapura, O. M., Чапура, О. М., Tarala, V. A., Тарала, В. А., Medyanik, E. V., Медяник, Е. В., Tarala, L. V., Тарала, Л. В., Suprunchuk, V. E., Супрунчук, В. Е., Malyavin, F. F., Малявин, Ф. Ф., Kuznetsov, S. V., Кузнецов, С. В., Lapin, V. A., Лапин, В. А.
Format:	Статья
Jezik:	English
Izdano:	Elsevier Ltd 2025
Teme:	Ceramics Thermal diffusivity Hot isostatic pressing LuAG Luminescence Optical properties
Online dostop:	https://dspace.ncfu.ru/handle/123456789/29617
Oznake:	Označite Brez oznak, prvi označite!

Opis
Izvleček:	Highly transparent ceramics based on LuAG with erbium content ranging from 1 to 50 at% were synthesized from powders prepared via chemical precipitation in an aqueous solution. The impact of hot isostatic pressing on the optical properties of these ceramics was investigated. It was demonstrated that employing hot isostatic pressing enhances the optical transmittance of LuAG:Er ceramics. The influence of erbium concentration on the average grain size of the ceramics was also examined. Additionally, temperature-dependent thermal diffusivity profiles of LuAG:Er ceramics as a function of erbium content were analyzed. Erbium concentrations yielding the highest luminescence intensity in spectral ranges around ∼1.5–1.6 μm and ∼2.7 μm were determined.

Fabrication and characterization of LuAG: Er ceramics with high optical transmission

Podobne knjige/članki