Nucleation and growth of YAG: Yb crystallites: a step towards the dispersity control

Nucleation and growth of YAG: Yb crystallites: a step towards the dispersity control

In this work, the dynamics of changing the ceramic powder phase composition and the size of garnet crystallites during calcination of the precursor at various temperature and time conditions were studied on the example of YAG: Yb oxide composition. The precursor powder was synthesized by the chemica...

وصف كامل

محفوظ في:
التفاصيل البيبلوغرافية
المؤلفون الرئيسيون: Kravtsov, A. A., Кравцов, А. А., Chikulina, I. S., Чикулина, И. С., Tarala, V. A., Тарала, В. А., Vakalov, D. S., Вакалов, Д. С., Nikova, M. S., Никова, М. С., Malyavin, F. F., Малявин, Ф. Ф., Krandievsky, S. O., Крандиевский, С. О., Blinov, A. V., Блинов, А. В., Lapin, V. A., Лапин, В. А.
التنسيق: Статья
اللغة:English
منشور في: Elsevier Ltd 2020
الموضوعات:
Ceramic powder
Dispersity control
Growth
Nucleation
Particles
YAG
Yb ceramics
Ytterbium compounds
الوصول للمادة أونلاين:https://dspace.ncfu.ru/handle/20.500.12258/13678
الوسوم: إضافة وسم
لا توجد وسوم, كن أول من يضع وسما على هذه التسجيلة!

الانترنت

https://dspace.ncfu.ru/handle/20.500.12258/13678

مواد مشابهة