Nucleation and growth of YAG: Yb crystallites: a step towards the dispersity control

Nucleation and growth of YAG: Yb crystallites: a step towards the dispersity control

In this work, the dynamics of changing the ceramic powder phase composition and the size of garnet crystallites during calcination of the precursor at various temperature and time conditions were studied on the example of YAG: Yb oxide composition. The precursor powder was synthesized by the chemica...

সম্পূর্ণ বিবরণ

সংরক্ষণ করুন:
গ্রন্থ-পঞ্জীর বিবরন
প্রধান লেখক: Kravtsov, A. A., Кравцов, А. А., Chikulina, I. S., Чикулина, И. С., Tarala, V. A., Тарала, В. А., Vakalov, D. S., Вакалов, Д. С., Nikova, M. S., Никова, М. С., Malyavin, F. F., Малявин, Ф. Ф., Krandievsky, S. O., Крандиевский, С. О., Blinov, A. V., Блинов, А. В., Lapin, V. A., Лапин, В. А.
বিন্যাস: Статья
ভাষা:English
প্রকাশিত: Elsevier Ltd 2020
বিষয়গুলি:
Ceramic powder
Dispersity control
Growth
Nucleation
Particles
YAG
Yb ceramics
Ytterbium compounds
অনলাইন ব্যবহার করুন:https://dspace.ncfu.ru/handle/20.500.12258/13678
ট্যাগগুলো: ট্যাগ যুক্ত করুন
কোনো ট্যাগ নেই, প্রথমজন হিসাবে ট্যাগ করুন!

আন্তর্জাল

https://dspace.ncfu.ru/handle/20.500.12258/13678

অনুরূপ উপাদানগুলি