The scandium impact on the sintering of YSAG:Yb ceramics with high optical transmittance

Optical ceramics based on Yb2O3–Y2O3-Sc2O3–Al2O3 solid solutions with a garnet structure were obtained using chemical precipitation and vacuum sintering techniques. In the samples' composition, scandium was incorporated into both dodecahedral and octahedral garnet sites in ratios from 4: 1 to 1...

תיאור מלא

שמור ב:

מידע ביבליוגרפי
Главные авторы:	Nikova, M. S., Никова, М. С., Tarala, V. A., Тарала, В. А., Malyavin, F. F., Малявин, Ф. Ф., Vakalov, D. S., Вакалов, Д. С., Lapin, V. A., Kuleshov, D. S., Кулешов, Д. С., Kravtsov, A. A., Кравцов, А. А., Chikulina, I. S., Чикулина, И. С., Tarala, L. V., Тарала, Л. В., Evtushenko, E. A., Евтушенко, Е. А., Medyanik, E. V., Медяник, Е. В., Krandievsky, S. O., Крандиевский, С. О., Лапин, В. А.
פורמט:	Статья
שפה:	English
יצא לאור:	Elsevier Ltd 2020
נושאים:	Garnets Optical ceramics Scandium Vacuum sintering YSAG:Yb Ytterbium compounds
גישה מקוונת:	https://dspace.ncfu.ru/handle/20.500.12258/14199
תגים:	הוספת תג אין תגיות, היה/י הראשונ/ה לתייג את הרשומה!

אינטרנט

https://dspace.ncfu.ru/handle/20.500.12258/14199

The scandium impact on the sintering of YSAG:Yb ceramics with high optical transmittance

אינטרנט

פריטים דומים