Impact of magnesium oxide concentration and yttrium-aluminum garnet stoichiometry deviation on the microstructure and optical transmission of yag-based ceramics

Impact of magnesium oxide concentration and yttrium-aluminum garnet stoichiometry deviation on the microstructure and optical transmission of yag-based ceramics

The paper investigates the effect of the magnesium oxide concentration on the ceramics’ microstructure and optical transmittance under conditions of excess Al3+ (4.8 mol.%) and Y3+ (2.9 mol.%) cations in the garnet structure, as well as the stoichiometric ratio Y3+/Al3+ = 3/5. Samples of optical cer...

وصف كامل

محفوظ في:
التفاصيل البيبلوغرافية
المؤلفون الرئيسيون: Malyavin, F. F., Малявин, Ф. Ф., Kravtsov, A. A., Кравцов, А. А., Tarala, V. A., Тарала, В. А., Nikova, M. S., Никова, М. С., Chikulina, I. S., Чикулина, И. С., Vakalov, D. S., Вакалов, Д. С., Lapin, V. A., Лапин, В. А., Kuleshov, D. S., Кулешов, Д. С., Medyanik, E. V., Медяник, Е. В.
التنسيق: Статья
اللغة:English
منشور في: ITMO University 2022
الموضوعات:
Stoichiometry
Yttrium-aluminum garnet
Average grain size
Microstructure
Optical ceramics
Vacuum sintering
الوصول للمادة أونلاين:https://dspace.ncfu.ru/handle/20.500.12258/18581
الوسوم: إضافة وسم
لا توجد وسوم, كن أول من يضع وسما على هذه التسجيلة!

الانترنت

https://dspace.ncfu.ru/handle/20.500.12258/18581

مواد مشابهة