Impact of magnesium oxide concentration and yttrium-aluminum garnet stoichiometry deviation on the microstructure and optical transmission of yag-based ceramics

The paper investigates the effect of the magnesium oxide concentration on the ceramics’ microstructure and optical transmittance under conditions of excess Al3+ (4.8 mol.%) and Y3+ (2.9 mol.%) cations in the garnet structure, as well as the stoichiometric ratio Y3+/Al3+ = 3/5. Samples of optical cer...

תיאור מלא

שמור ב:

מידע ביבליוגרפי
Главные авторы:	Malyavin, F. F., Малявин, Ф. Ф., Kravtsov, A. A., Кравцов, А. А., Tarala, V. A., Тарала, В. А., Nikova, M. S., Никова, М. С., Chikulina, I. S., Чикулина, И. С., Vakalov, D. S., Вакалов, Д. С., Lapin, V. A., Лапин, В. А., Kuleshov, D. S., Кулешов, Д. С., Medyanik, E. V., Медяник, Е. В.
פורמט:	Статья
שפה:	English
יצא לאור:	ITMO University 2022
נושאים:	Stoichiometry Yttrium-aluminum garnet Average grain size Microstructure Optical ceramics Vacuum sintering
גישה מקוונת:	https://dspace.ncfu.ru/handle/20.500.12258/18581
תגים:	הוספת תג אין תגיות, היה/י הראשונ/ה לתייג את הרשומה!

אינטרנט

https://dspace.ncfu.ru/handle/20.500.12258/18581

Impact of magnesium oxide concentration and yttrium-aluminum garnet stoichiometry deviation on the microstructure and optical transmission of yag-based ceramics

אינטרנט

פריטים דומים