Sintering and microstructure evolution of Er1.5Y1.5-xScx+yAl5-yO12 garnet ceramics with scandium in dodecahedral and octahedral sites

Sintering and microstructure evolution of Er1.5Y1.5-xScx+yAl5-yO12 garnet ceramics with scandium in dodecahedral and octahedral sites

The sintering behavior of scandium-containing garnet materials within the Y2O3-Er2O3-Sc2O3-Al2O3 system was investigated. Single-phase ceramic powders and optical ceramics’ samples of Er1.5Y1.5-xScxScyAl5-yO12 (x = 0.2 ÷ 1.5; y = 0.2 ÷ 0.8) were prepared. An increase of scandium content in the dodec...

সম্পূর্ণ বিবরণ

সংরক্ষণ করুন:
গ্রন্থ-পঞ্জীর বিবরন
প্রধান লেখক: Nikova, M. S., Никова, М. С., Tarala, V. A., Тарала, В. А., Malyavin, F. F., Малявин, Ф. Ф., Chikulina, I. S., Чикулина, И. С., Vakalov, D. S., Вакалов, Д. С., Kravtsov, A. A., Кравцов, А. А., Krandievsky, S. O., Крандиевский, С. О., Lapin, V. A., Лапин, В. А., Medyanik, E. V., Медяник, Е. В.
বিন্যাস: Статья
ভাষা:English
প্রকাশিত: Elsevier Ltd 2022
বিষয়গুলি:
Erbium
Scandium
Garnet
Optical ceramics
Sintering behaviour
Aluminum oxide
অনলাইন ব্যবহার করুন:https://dspace.ncfu.ru/handle/20.500.12258/18613
ট্যাগগুলো: ট্যাগ যুক্ত করুন
কোনো ট্যাগ নেই, প্রথমজন হিসাবে ট্যাগ করুন!

আন্তর্জাল

https://dspace.ncfu.ru/handle/20.500.12258/18613

অনুরূপ উপাদানগুলি