Sintering and microstructure evolution of Er1.5Y1.5-xScx+yAl5-yO12 garnet ceramics with scandium in dodecahedral and octahedral sites

The sintering behavior of scandium-containing garnet materials within the Y2O3-Er2O3-Sc2O3-Al2O3 system was investigated. Single-phase ceramic powders and optical ceramics’ samples of Er1.5Y1.5-xScxScyAl5-yO12 (x = 0.2 ÷ 1.5; y = 0.2 ÷ 0.8) were prepared. An increase of scandium content in the dodec...

Πλήρης περιγραφή

Αποθηκεύτηκε σε:

Λεπτομέρειες βιβλιογραφικής εγγραφής
Κύριοι συγγραφείς:	Nikova, M. S., Никова, М. С., Tarala, V. A., Тарала, В. А., Malyavin, F. F., Малявин, Ф. Ф., Chikulina, I. S., Чикулина, И. С., Vakalov, D. S., Вакалов, Д. С., Kravtsov, A. A., Кравцов, А. А., Krandievsky, S. O., Крандиевский, С. О., Lapin, V. A., Лапин, В. А., Medyanik, E. V., Медяник, Е. В.
Μορφή:	Статья
Γλώσσα:	English
Έκδοση:	Elsevier Ltd 2022
Θέματα:	Erbium Scandium Garnet Optical ceramics Sintering behaviour Aluminum oxide
Διαθέσιμο Online:	https://dspace.ncfu.ru/handle/20.500.12258/18613
Ετικέτες:	Προσθήκη ετικέτας Δεν υπάρχουν, Καταχωρήστε ετικέτα πρώτοι!

Διαδίκτυο

https://dspace.ncfu.ru/handle/20.500.12258/18613

Sintering and microstructure evolution of Er1.5Y1.5-xScx+yAl5-yO12 garnet ceramics with scandium in dodecahedral and octahedral sites

Διαδίκτυο

Παρόμοια τεκμήρια