The dependence of aluminum nitride thin-film microstructure on the number of low-temperature plasma-enhanced atomic layer deposition process cycles

The dependence of aluminum nitride thin-film microstructure on the number of low-temperature plasma-enhanced atomic layer deposition process cycles

Within the framework of the study, oriented aluminum nitride coatings were obtained on sapphire with orientation along the direction (0001) using the PEALD method at a temperature of 250°С and a number of deposition cycles from 80 to 500. The obtained samples were studied using ellipsometry, X-ray d...

وصف كامل

محفوظ في:
التفاصيل البيبلوغرافية
المؤلفون الرئيسيون: Ambartsumov, M. G., Амбарцумов, М. Г., Tarala, V. A., Тарала, В. А., Krandievsky, S. O., Крандиевский, С. О., Kravtsov, A. A., Кравцов, А. А., Saytiev, A. B., Саутиев, А. Б., Mitrofanenko, L. M., Митрофаненко, Л. М.
التنسيق: Статья
اللغة:English
منشور في: Elsevier B.V. 2019
الموضوعات:
AFM
AlN
Atomic layer deposition
Ellipsometry
PEALD
X-ray diffraction
Aluminum coated steel
Aluminum nitride
Atomic force microscopy
Aluminum coatings
الوصول للمادة أونلاين:https://www.scopus.com/record/display.uri?eid=2-s2.0-85075729953&origin=resultslist&sort=plf-f&src=s&st1=The+dependence+of+aluminum+nitride+thin-film+microstructure+on+the+number+of+low-temperature+plasma-enhanced+atomic+layer+deposition+process+cycles&st2=&sid=74064f1f4b25bf0f5642e6da8f07737a&sot=b&sdt=b&sl=162&s=TITLE-ABS-KEY%28The+dependence+of+aluminum+nitride+thin-film+microstructure+on+the+number+of+low-temperature+plasma-enhanced+atomic+layer+deposition+process+cycles%29&relpos=0&citeCnt=0&searchTerm=
https://dspace.ncfu.ru/handle/20.500.12258/9109
الوسوم: إضافة وسم
لا توجد وسوم, كن أول من يضع وسما على هذه التسجيلة!
الوصف
الملخص:Within the framework of the study, oriented aluminum nitride coatings were obtained on sapphire with orientation along the direction (0001) using the PEALD method at a temperature of 250°С and a number of deposition cycles from 80 to 500. The obtained samples were studied using ellipsometry, X-ray diffraction, and atomic force microscopy. It was shown that with an increase in the thickness of the coating, the refraction index increases to 2.02, and the root-mean-square (RMS) increases from 0.35 to 2.35 nm. All samples had (0002) and (0004) reflexes on X-ray diffractograms measured in the Bragg-Brentano geometry (θ/2θ-scan). On Δω-scans of the reflex (0002), the full width at half maximum (FWHM) amounted to 162 ± 7 arcsec

مواد مشابهة